CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
| COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
| LEGA PRESS AFFINATO UNI EN 1982:2008 CB754S | 58-62 | 0.5-2.4 | 1 max | 0.7 max | 0.5 max | 1 max | 0.05 max | 0.10-0.8 | Resto | 0.02 max | ||
|
|||||||||||||||||||||||
| COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS | WorkabilityTtool % Over Bar OT | Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | |||||||||||||
| LEGA PRESS AFFINATO UNI EN 1982:2008 CB754S | 8.45 | 21 | 80 | 1.9-2 | 980-1080 | 890 | 220/280 | 80/120 | 15 | 70/110 | |||||||||||||