CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
| COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
| OT-B BASSA PRESSIONE UNI EN 1982-2008-CB755S | 59-60.5 | 1.2-1.7 | 0.2 max | 0.05-0.2 max | 0.05 max | 0.3 max | 0.03 max | 0.4-0.65 | Resto | |||
|
PHYSICAL AND MECHANICAL |
|||||||||||
| COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS | WorkabilityTtool % Over Bar OT | Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | |
| OT-B BASSA PRESSIONE UNI EN 1982-2008-CB755S | 8.4 | 21 | 80 | 1.9-2 | 980-1080 | 890 | 350 min | 180 min | 13 min | 90 min | |