CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
| COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
| OT-SI CU63 ARTISTICA UNI EN 1982:2008 CB 751S | 62-64 | 1.5-2 | 0.5 max | 0.6 max | 0.1 max | 0.7 max | 0.7-1 | 0.3-0.5 | Resto | |||
| OT-SI CU 65 ARTISTICA
UNI EN 1982:2008 CB 751S |
64-65.5 | 1.5-2 | 0.4 max | 0.5 max | 0.1 max | 0.7 max | 0.7-1 | 0.3-0.5 | Resto | |||
|
PHYSICAL AND MECHANICAL |
|||||||||||
| COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS | WorkabilityTtool % Over Bar OT | Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | |
| OT-SI CU63 ARTISTICA UNI EN 1982:2008 CB 751S | 8.4 | 15 | 85 | 1.8-1.9 | 1020-1100 | 900 | 370-430 | 150/190 | 23/29 | 90/110 | |
| OT-SI CU 65 ARTISTICA UNI EN 1982:2008 CB 751S | 8.42 | 15 | 85 | 1.8-1.9 | 1020.1100 | 900 | 380/430 | 180/230 | 15/22 | 95/110 | |