CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
| COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
| OT-A UNI EN 1982:2017-CB753S | 58-60 | 1.8-2.5 | 0.5-1.2 | 0.5-0.8 | 0.2 max | 0.8 max | 0.05 max | 0.4-0.8 | Resto | 0.05 | 0.02 max | |
|
PHYSICAL AND MECHANICAL |
|||||||||||
| COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS |
WorkabilityTtool % Over Bar OT
|
Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | |
| OT-A UNI EN 1982:2017-CB753S | 8.4 | 21 | 80 | 1.9-2 | 980-1080 | 890 | 300 min | 150 min | 15 min | 90 min | |